Ceiling Board Fire Retardant Board 1220mmx3050mx9mm Grade B1-B

• Customization: Available
• After-sales Service: Well
• Warranty: 1 Year
• Model NO.: FR MDF
• Material: Wood Fiber
• Type: Fire Retardant Board
• Finish: Without Decoration
• Formaldehyde Emission Standards: E1
• Usage: Indoor, Decoration
• Production Process: Dry-Proces
• Size: 1220X3050
• Thickness: 9mm
• Certification: ISO, GB
• Color: Red
• Quality: Export Standard
• Payment Term: Fob, CIF, 30% T/T in Advance, L/C at Sight
• Density: 740~850kg/M3
• Glue: Fsc/Carb/E0/E1/E2
• Using: Construction, Furniture, Decoration
• Transport Package: Pallet Packing
• Specification: POPLAR
• Trademark: HUQIAN
• Origin: China
• HS Code: 441114
• Production Capacity: 2000 PCS/Day

Product Description

Description:
Homogeneous characteristics
Low swelling in thickness
Smooth surface
Suitable for surfaces applications (melamine facing, foil, veneer, etc.)
Fire Retardant MDF are non-load-bearing boards with improved fire retardant properties and are manufactured in compliance with GB 8624-2012(same standard as EN_13501-1 where they are defined as boards for general use in dry conditions.

Category:
SIZE: 1220mmX3050mm
Thickness: 3mm, 5mm, 9mm, 12mm, 15mm,18mm
GRADE: B1-B, B1-C

HUQIAN GROUP has imported Germany Siempelkamp continuous press---- Austria Andritz thermofiner----American GTS energy plant, to assure the stable & excellenct quality to client.

PRODUCT SPEC:

Product Models:	3050MMx1220MMx9MM FIRE RETARDANT BOARD GRADE B1-B
	Glue: E1			Seeds of trees: Poplar
	Grinding Machine: Import Machine			Sanding:  YES
Physical Parameter:	Density:756kg/m3			Moisture Content: 5.1%
	Elasticity Modulus:2812MPA			Surface soundness: 1.3MPA
	Bending Strength: 29.5MPA			Thickness swelling: 19%
	Internal Bond: 0.98MPA

Application:
uring the manufacturing process, the flame retardant additive is blended with the fiber throughout the panel.
This process delivers superior performance versus topical flame retardant applications. In addition, FR MDF can be machined, cut, sanded, and grooved without compromising the flame retardance.